Effects of multipurpose, universal adhesives on resin bonding to zirconia ceramic

Abstract

This study evaluated the effects of singlebottle, multipurpose, universal adhesives on the bond strength of resin cement to zirconia ceramic. Polished zirconia ceramic (Cercon base) discs were randomly divided into four groups (n=40) according to the applied surface- conditioning agent: Single Bond 2, Single Bond Universal, All-Bond Universal, and Alloy Primer. Cured composite cylinders (Ø 0.8 mm3 1 mm) were cemented to the conditioned zirconia specimens with resin cement (RelyX ARC). The bonded specimens were subjected to a microshear bond-strength test after 24 hours of water storage and after 10,000 cycles of thermocycling. The surface-conditioning agent significantly influenced the bond strength (p<0.05). Single Bond Universal showed the highest initial bond strength (37.7 ± 5.1 MPa), followed by All-Bond Universal (31.3 ± 5.6 MPa), Alloy Primer (26.9 ± 5.1 MPa), and Single Bond 2 (8.5 ± 4.6 MPa). Artificial aging significantly reduced the bond strengths of all the test groups (p<0.05). After 10,000 cycles of thermocycling, All-Bond Universal showed the highest bond-strength value (26.9 ± 6.4 MPa). Regardless of artificial aging, Single Bond Universal and All-Bond Universal showed significantly higher bond strengths than Alloy Primer, a conventional metal primer.