Influence of cyclic loading on the fracture toughness and load bearing capacities of all-ceramic crowns

Abstract

The purpose of this study was to investigate how cyclic loading influenced the fracture toughness of hot-press lithium disilicate and zirconia core materials and whether there was an increase in the propensity for crown failure. Two types of all-ceramic crowns including the IPS e.max Press system (n=24) and the Lava zirconia system (n=24), were selected. Sectioned specimens were subjected to cyclic loading with the maximum magnitude of 200 N (R=0.1) until two million cycles. The material properties including Young's modulus (E) and hardness (H) and the fracture toughness (KIC) of the core materials were evaluated using indentation methods (n=12 each). The load-bearing capacities of the specimens were examined by means of monotonic load to fracture (n=12 each). It was found that the material properties, including E, H and KIC, of the two types of dental ceramics, were reduced. Statistical analysis indicated that there were no significant influences of fatigue loading on material properties E and H for both types of dental ceramics or K IC for zirconia, while for the IPS e.max Press core, KIC, which was parallel to the direction of the lithium disilicate crystals, was significantly reduced (P=0.001). A conclusion was drawn that zirconia possesses high mechanical reliability and sustainable capacity to resist fatigue loading, while fatigue loading remarkably degraded the anisotropic mechanical behaviour of hot-press lithium disilicate ceramics. © 2014 WCSS.