Structure-properties relationship in trip type bainitic ferrite steel austempered at different temperatures

Abstract

Background: Attractive properties of TRIP-type bainitic ferrite (TBF) steel ascribe to its unique microstructure of lath structure bainitic ferrite matrix and interlath retained austenite films. This work is concerned with obtaining ultra high-strength hot forged TBF steel with high elongation and excellent strength-elongation balance. Methods: The effect of austempering temperature on the microstructure along with its retained austenite characteristics and tensile properties of a hot forged TBF steel was studied. A detailed investigation correlating the steel structure and its tensile properties was carried out. Results: Tensile strength ranging from 1058 to 1552 MPa was achieved when the hot forged steel was austempered at (325-475 °C). Conclusions: Ultra high tensile strength of 1058 MPa, large total elongation of 29% and excellent strength-elongation balance of 30 GPa % were attained when the steel was austempered at 425 °C. The large total elongation of this steel is mainly due to the uniform fine lath structure matrix and the pronounced TRIP effect of a large amount of retained austenite films which prevents a rapid decrease of strain hardening rate at low strain and leads to a relatively high strain hardening at high strain level. Rapid transformation of blocky retained austenite at low strain in the hot forged TBF steel austempered at higher temperatures results in a rapid increase of initial strain hardening. In addition, the coarse microstructure that contains large blocks of retained austenite / martensite and the insufficient numbers of bainitic ferrite lathes and retained austenite films deteriorate the total elongation and the strength-elongation balance of the TBF austempered at 475 °C.