Effect of zirconium addition to austenitic stainless steels on suppression of radiation induced chromium segregation at grain boundaries under ion irradiation

Abstract

The effect of Zr addition to austenitic stainless steels on the suppression of radiation induced Cr segregation at grain boundaries under 400 keV He+ irradiation was studied. Type 316L stainless steel and steels with addition of 0.07, 0.21 or 0.41 mass% Zr were kept at 1,423K for 30 min, and then they were quenched into the water. Irradiation was done at 773K with the dose rate of 2.4×10−4dpa/s. The total dose was 0.85 or 3.4dpa. After irradiation, profiles of Cr concentration across the grain boundaries were measured using an analytical electron microscope with 1 nm beam diameter. Concentration of Cr at the grain boundary is decreased by radiation induced segregation. However, it increased with the addition of Zr, and the Cr segregation is almost completely suppressed when Zr is added more than 0.21 mass%. The effect of Zr addition on suppression of Cr segregation was analyzed focussing on the interaction between dissolved Zr atoms and point defects. The effect is based on vacancy trapping by the Zr atom, and the extent to which it suppresses Cr segregation can be empirically evaluated using a radiation induced segregation model by changing the effective vacancy migration energy. © 1996 Taylor and Francis Group, LLC.