The Effect of Crevice Structure on Corrosion Behavior of P110 Carbon Steel in a Carbonated Simulated Concrete Environment

Abstract

This study systematically investigated the corrosion behavior of P110 pipeline steel in simulated carbonated concrete environments through a combination of electrochemical testing and multiphysics simulation, with particular focus on revealing the evolution mechanisms of corrosion product deposition and ion concentration distribution under half crevice structures, providing new insights into localized corrosion in concealed areas. Experimental results showed that no significant corrosion occurred on the P110 steel surface in uncarbonated simulated pore solution. Conversely, the half crevice structure significantly promoted the development of localized corrosion in carbonated simulated pore solution, with the most severe corrosion and substantial accumulation of corrosion products observed at the crevice mouth region. COMSOL Multiphysics simulations demonstrated that this phenomenon was primarily attributed to local enrichment of Cl− and H+ ions, leading to peak corrosion current density, and directional migration of Fe2+ ions toward the crevice mouth, causing preferential deposition of corrosion products at this location. This “electrochemical acceleration-corrosion product deposition” multiphysics coupling analysis of corrosion product deposition patterns within crevices represents a new perspective not captured by traditional crevice corrosion models. The established ion migration-corrosion product deposition model provides new theoretical foundations for understanding crevice corrosion mechanisms and predicting the service life of buried concrete pipelines.