High-voltage vertical Ga2O3 power rectifiers operational at high temperatures up to 600 K

66Citations
Citations of this article
42Readers
Mendeley users who have this article in their library.
Get full text

Abstract

This work presents the temperature-dependent forward conduction and reverse blocking characteristics of a high-voltage vertical Ga2O3 power rectifier from 300 K to 600 K. Vertical β-Ga2O3 Schottky barrier diodes (SBDs) were fabricated with a bevel-field-plated edge termination, where a beveled sidewall was implemented in both the mesa and the field plate oxide. The Schottky barrier height was found to increase from 1.2 eV to 1.3 eV as the temperature increases from 300 K to 600 K, indicating the existence of barrier height inhomogeneity. The net donor concentration in the drift region shows little dependence on the temperature. The reverse leakage current up to 500 V was found to be limited by both the thermionic-field electron injection at the Schottky contact and the electron hopping via the defect states in the depletion region. At 300-500 K, the leakage is first limited by the electron injection at low voltages and then by the hopping in depleted Ga2O3 at high voltages. At temperatures above 500 K, the thermionic field emission limits the device leakage over the entire voltage range up to 500 V. Compared to the state-of-the-art SiC and GaN SBDs when blocking a similar voltage, our vertical Ga2O3 SBDs are capable of operating at significantly higher temperatures and show a smaller leakage current increase with temperature. This shows the great potential of Ga2O3 SBDs for high-temperature and high-voltage power applications.

Cite

CITATION STYLE

APA

Wang, B., Xiao, M., Yan, X., Wong, H. Y., Ma, J., Sasaki, K., … Zhang, Y. (2019). High-voltage vertical Ga2O3 power rectifiers operational at high temperatures up to 600 K. Applied Physics Letters, 115(26). https://doi.org/10.1063/1.5132818

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free