Optical, structural, and chemical properties of flash evaporated In 2S3 buffer layer for Cu(In,Ga)Se2 solar cells

Abstract

In2S3 layers were deposited by flash evaporation technique with varying flash rates. The optical constants of layers based on Tauc-Lorentz model dielectric function were extracted from spectroscopic ellipsometry measurements. X-ray photoelectron spectroscopic investigation revealed the presence of oxygen impurity in as-deposited and air-annealed layers with traces of Na inclusion in the layer grown at high flash rate. The enhancement in crystalline arrangement of as-deposited layer after air annealing was confirmed by Raman spectroscopy. Rutherford backscattering measurements revealed the growth of off-stoichiometric layers at all flash rates. An analytical layer growth model has been proposed supporting the results obtained by various layer characterization techniques. The solar cells were prepared with flash evaporated In2S3 buffer layers and their performances were compared with CdS reference solar cell. A significant gain in short-circuit current was obtained after air annealing of the complete device at 200 °C for 20 min. A maximum conversion efficiency of 12.6% was delivered by a high flash rate In2S3 buffered cell with open-circuit voltage close to that of CdS reference cell. The improvement in device performance after air annealing treatment is explained by thermally enhanced Cu and oxygen diffusion from Cu (In,Ga) Se2 and i-ZnO to In 2S3 layer, respectively. © 2010 American Institute of Physics.