Atmospheric Plasma Spraying of Al 2 O 3 + 13% TiO 2 Coatings Using External and Internal Injection System

Abstract

The ceramic coatings based on mixture of Al 2 O 3 and TiO 2 have better properties in comparison to the pure alumina ones. Among many techniques, plasma spraying is very useful method of ceramic coatings manufacturing. In this paper, the results of microscopic, mechanical and tribological properties investigations of Al 2 O 3 + 13 wt% TiO 2 coatings manufactured by atmospheric plasma spraying are presented. The cylinder substrates made from stainless steel (X5CrNi18-10) had a diameter equal to 25 mm and thickness equal to 2 mm. The plasma spray experimental parameters included three variables: (i) type of injection system (external or internal), (ii) size of corundum particles for sandblasting and (iii) torch linear speed. The results confirm, that type of injection system is a dominant parameter. Internal injection results in better degree of particles melting, what influences on wear resistance performance, as well as higher values of bond strength.