Fused Filament Fabrication of Poly (Lactic Acid) Reinforced with Silane-Treated Cellulose Fiber for 3D Printing

Abstract

Various polylactic acid (PLA) blends were reinforced with untreated or silane-treated micro-sized cellulose fiber (MCF), successfully prepared as 3D printing filaments and then printed using a fused filament fabrication (FFF) 3D printer. In this study, we focused on developing 3D-printed MCF/PLA composites through silane treatment of MCF and investigating the effect of silane treatment on the various properties of FFF 3D-printed composites. Fourier transform infrared spectra confirmed the increase in hydrophobic properties of silane-treated MCF by showing the new absorption peaks at 1,100 cm-1, 1,030 cm-1, and 815 cm-1 representing C-NH2, Si-O-Si, and Si-CH2 bonds, respectively. In scanning electron microscope images of silane-treated MCF filled PLA composites, the improved interfacial adhesion between MCF and PLA matrix was observed. The mechanical properties of the 3D-printed MCF/PLA composites with silane-treated MCF were improved compared to those of the 3D-printed MCF/PLA composites with untreated MCF. In particular, the highest tensile and flexural modulus values were observed for S-MCF10 (5,784.77 MPa) and S-MCF5 (2,441.67 MPa), respectively. The thermal stability of silane-treated MCF was enhanced by delaying the initial thermal decomposition temperature compared to untreated MCF. The thermal decomposition temperature difference at T95 was around 26°C. This study suggests that the effect of silane treatment on the 3D-printed MCF/PLA composites is effective and promising.