The Effect of Multiple Factors on the Fatigue Crack Growth Behavior of DH36 Steel in Arctic Environment

Abstract

In Arctic regions, ship structures face low temperatures, overloads, thickness effects, and fluctuating stress ratios, which significantly influence the fatigue crack growth (FCG) behavior of marine steels. This study investigates the FCG behaviors of DH36 steel by a series of experiments under the combined effects of low temperatures, overload ratios Rol, specimen thickness B, and stress ratios R. Experiment results show that the yield strength, ultimate tensile strength, and elastic modulus of DH36 steel exhibit negative correlations with temperature varying within the Arctic temperature range. A reduction in fatigue crack growth rate (FCGR) is observed under the combined effects of low temperature and overload, and the magnitude of decrease shows a positive correlation with Rol. Notably, low temperatures weaken the FCG retardation effect induced by overload, and this attenuation becomes more pronounced as temperature decreases. Under low temperatures, while maintaining constant peak load, increasing R significantly reduces both initial and terminal stress intensity factor ranges ΔK0 and ΔKe, resulting in diminished effective crack driving force and thereby substantially extending FCG life. Although increased B enhances FCGR at low temperatures, thinner plates demonstrate shorter FCG life due to their higher ΔK0 values.