Catalytic Degradation of Methylene Blue Using Cellulose Acetate Composite Membrane Fabricated with Nickel Nanoparticles

Abstract

Environmental contamination from industrial dyes, particularly Methylene Blue (MB), presents a growing challenge due to their toxicity and persistence in aquatic systems. This study explored the catalytic potential of cellulose acetate-stabilized nickel (CA/Ni) nanoparticles for the degradation of MB in aqueous solutions. CA/Ni was synthesized and characterized using FTIR and SEM, confirming its successful incorporation into the cellulose acetate matrix and uniform distribution across the membrane. UV-Vis spectrophotometry was employed to monitor the catalytic degradation of MB, revealing a significant decrease in absorbance at 665 nm over 28 min, indicating 68% degradation efficiency. Kinetic analysis showed that the degradation followed pseudo-first-order kinetics, with an apparent rate constant of 0.0348 min−1 and an R2 value of 0.9851, confirming excellent catalytic performance. The effects of temperature and pH on MB degradation were investigated, with the highest efficiency observed at 35 °C and a pH of 7. A room temperature (25 °C) and acidic conditions (pH 5) reduced the degradation rate to 52%. In comparison, a higher temperature (45 °C) and an alkaline pH (pH 9) resulted in a slight decline to 55%, likely due to changes in catalyst efficiency and MB solubility. These findings highlight the potential of Ni NP-stabilized membranes for wastewater treatment applications, providing a scalable and efficient approach to dye removal.