Preparation and Properties of Boron Nitride or Aluminum Nitride Reinforced Glass Fiber/Modified Polyphenylene Sulfide Composites

Abstract

In this work, polyphenylene sulfide (PPS) containing carboxyl group was synthesized and used to prepare PPS-2COOH/LGF/AlN and composites with high-temperature resistance, corrosion resistance, low dielectric constant, and low dielectric loss were prepared with boron nitride/aluminum nitride (BN/AlN) and glass fiber (LGF). The results showed that the introduction of carboxyl groups did not affect the structure and thermal properties of PPS. The composites exhibited good mechanical properties with a tensile strength of 65 MPa97 MPa and flexural strength of 112 MPa154 MPa. The TGA results showed that the composites had good thermal stability, and the T5% of PPS-2COOH/LGF/AlN (20) and PPS-2COOH/LGF/BN (20) reached up to 511.6°C and 506.3°C, respectively. They were insoluble in some organic solvents, such as NMP and DMF at room temperature, and they exhibited excellent chemical resistance. The dielectric performance results showed that with the increase of frequency, the dielectric constant and dielectric loss gradually decreased, the dielectric constant of PPS-2COOH/LGF/BN (15) was 3.9, and the dielectric loss of PPS-2COOH/LGF/BN (15) was 0.01. From the above results, it can be concluded that the composite materials PPS-2COOH/LGF/AlN and PPS-2COOH/LGF/BN have potential application prospects in the field of 5G high thermal conductivity materials.