Synthesis of Eugenol-Lauryl Methacrylate Copolymers via Cationic Polymerization

Abstract

Eugenol is one of the most abundant natural resources in Indonesia. The recently bio-based polymer resin is created based on eugenol because eugenol is functionalized with the polymerizable group. In order to improve the functional properties of eugenol, in this research Eugenol-Lauryl Methacrylate copolymers (co-poly(Eg-LMA)) were synthesized by cationic polymerization using H2SO4 as an initiator under the nitrogen atmosphere. Structure identification of the copolymer showed the absorption of the vinyl group from the monomers disappear at the analysis through FTIR at the wave number 1637-1639 and 985-995 cm-1 and also 1H-NMR on the chemical shift 5,97 and 5,08 ppm. The resulting copolymers obtained brown powder in 32.03 % yieldsand melting point at 96 - 97 °C. Solubility test of the co-poly(Eg-LMA) showed that the polymer couldnot soluble in water but soluble in chloroform, diethyl ether, and benzene. Average molecular weight of co-poly(Eg-LMA) Led Ostwald viscometry was obtained 42020 with the degree of polymerization by 200.