From transparent to black amorphous zinc oxide thin films through oxygen deficiency control

Abstract

Despite the fact that zinc oxide is a well-known transparent oxide, several recent studies on "black"ZnO have renewed its potential for photocatalytic applications. We report on the control of oxygen deficiency in ZnO thin films grown at 300 °C on c-cut sapphire single-crystal substrates by pulsed electron beam deposition (PED) through a slight variation of argon pressure in PED. At a pressure of 2 × 10-2 mbar transparent, stoichiometric (ZnO) and crystalline films are obtained, while at 9 × 10-3 mbar black, oxygen-deficient (ZnO0.85) and amorphous films result. Stoichiometry, structural, and optoelectronic properties of transparent and black ZnO thin films were comparatively analyzed as a function of oxygen deficiency. Black ZnO thin films exhibit enhanced absorption in the visible and near-infrared due to oxygen deficiency, thus extending the range of applications of zinc oxide thin films from transparent electronics to solar absorbers and photocatalysis.