Influence of cavo superficial enamel acid-etching on the microtensile bond strength of low-shrinkage composite resin

Abstract

Introduction: To prevent the shrinkage stresses produced during polymerization, composite resins of low polymerization shrinkage were developed. Objective: To evaluate the microtensile bond strength in class I cavities restored by acid-etching the cavosurface angle and with composite resins indicated for posterior teeth. Material and method: 48 healthy molars were selected and divided into six groups (n = 8), considering that the cavosurface enamel of three groups was etched with 35% phosphoric acid. The teeth were restored with the Clearfil SE Bond adhesive system and Filtek Z350 XT, Empress Direct, and Charisma Diamond composite resins, which were light-cured for 40 seconds. After 24 hours, the teeth were taken to a cutting machine, which produced sections in the buccolingual and mesiodistal directions. This resulted in toothpicks of 0.9×0.9 mm that were taken to the universal testing machine for the microtensile bond strength test. Statistical analysis was performed with ANOVA and Tukey’s test (p < 0.05). Result: There was no statistically significant difference between the groups evaluated. Conclusion: Acid-etching the cavosurface angle did not affect the performance of restorations, probably due to the adhesive system used.