Comparison of cellulose dissolution behavior by alkaline and sulfuric acid solvents and their films’ physical properties

Abstract

Three alkaline mixtures (NaOH/thiourea, NaOH/urea/thiourea, NaOH/urea/ZnO) and sulfuric acid were used at low temperatures as cellulose solvents, and their cellulose solubility and films’ physical properties for bleached chemical wood pulps and cotton linter were compared. Their degree of polymerization (DP) was controlled to 600–800 before dissolution. Among the alkaline solvents, NaOH/urea/ZnO gave the film the highest tensile strength and stretch. When compared to sulfuric acid, NaOH/urea/ZnO gave lower strength properties but higher crystallinity indices in the films. While alkaline solvents could not dissolve the high DP cellulose (DP ~ 2000), sulfuric acid could dissolve the high DP cellulose at below zero Celsius temperature, and the strength properties of the films were not much different from that of the low DP one. It appeared that the low-temperature sulfuric acid treatment did away with the cellulose’s DP controlling stage; it decreased cellulose DP very quickly for the high-DP cellulose at the initial stage, and as soon as the cellulose DP reached a DP low enough for dissolution, it began to dissolve the cellulose to result in stable cellulose solution.