Study on corrosion mechanism of different concentrations of na2so4 solution on early‐age cast‐in‐situ concrete

Abstract

The deterioration of early‐age concrete performance caused by SO42− internal diffusion in concrete is a critical factor of concrete durability. In this study, the mechanical properties, heat of hydration, and pore structure of early‐age cast‐in‐situ concrete with different sodium sulfate (Na2SO4) concentrations were studied. The mechanism of SO42− internal corrosion was evaluated by measuring the dynamic elastic modulus, compressive strength, and heat of hydration rate. Scanning electron microscopy, energy dispersive spectroscopy, X‐ray computed tomography, X‐ray diffrac-tion, thermogravimetry‐derivative thermogravimetry, and differential scanning calorimetry were applied to analyze microstructural variations and complex mineral assemblages of concrete sam-ples. The results indicated that during the hardening process of cast‐in‐situ concrete, Na2SO4 first promoted and then hindered the hydration rate of cement, and also hindered the early strength development of the cement. As the concentration of Na2SO4 solution increases, the corrosion prod-ucts of ettringite (AFt) and gypsum (Gyp) gradually increase, causing cross cracks in the concrete. The proportion of small and medium pores first increases and then decreases, and the large pores first decrease and then increase. The mechanical properties of concrete gradually decrease and di-minish the mechanical properties of the concrete (thereby accelerating the damage to the concrete).