Nanoarchitectonics of Ni/CeO2 Catalysts: The Effect of Pretreatment on the Low-Temperature Steam Reforming of Glycerol

Abstract

CeO2 nanosphere-supported nickel catalysts were prepared by the wetness impregnation method and employed for hydrogen production from glycerol steam reforming. The dried catalyst precursors were either reduced by H2 after thermal calcination or reduced by H2 directly without calcination. The catalysts that were reduced by H2 without calcination achieved a 95% glycerol conversion at a reaction temperature of only 475 °C, and the catalytic stability was up to 35 h. However, the reaction temperature required of catalysts reduced by H2 with calcination was 500 °C, and the catalysts was rapidly inactivated after 25 h of reaction. A series of physicochemical characterization revealed that direct H2 reduction without calcination enhanced the concentration of oxygen vacancies. Thus, the nickel dispersion was improved, the nickel nanoparticle size was reduced, and the reduction of nickel was increased. Moreover, the high concentration of oxygen vacancy not only contributed to the increase of H2 yield, but also effectively reduced the amount of carbon deposition. The increased active nickel surface area and oxygen vacancies synergistically resulted in the superior catalytic performance for the catalyst that was directly reduced by H2 without calcination. The simple, direct hydrogen reduction method remarkably boosts catalytic performance. This strategy can be extended to other supports with redox properties and applied to heterogeneous catalytic reactions involving resistance to sintering and carbon deposition.