Structure, Spectra, Morphology, and Magnetic Properties of Nb5+ Ion-Substituted Sr Hexaferrites

Abstract

SrFe12−x Nbx O19 (x = 0.00–0.15) was here synthesized by a conventional solid-state reaction method. Thermogravimetry and differential scanning calorimetry curves revealed the sample reactions at four temperature ranges, and the optimal reaction stability was obtained at 1240◦ C. A single-phase polycrystalline form of SrFe12 O19 was obtained until the substitution reached 0.09, and the average crystallite size was found to be in the range of 44.21–60.02 nm. According to Fourier-transform infrared spectra, the formation of Fe–O bonds occurred at 69 and 450 cm−1 in the M-type ferrite, while Raman spectra revealed that all the peaks in the sample corresponded to Raman vibration modes and M-type structures. Through the shift of the peaks, it is speculated that Nb5+ enters into the lattice. The hysteresis loops of the samples were measured by vibrating-sample magnetometry, and the calculated results demonstrated that the coercivity increased with increases in the doping amount (686.3 Oe). At the same time, the saturation magnetization remained at a large value (>72.49 emu/g), which has rarely been reported.