Effect of Grazing Angle Cross-Ion Irradiation on Ag Thin Films

9Citations
Citations of this article
5Readers
Mendeley users who have this article in their library.

Abstract

© 2016, The Author(s). Apart from the spherical shape, control over other shapes is a technical challenge in synthesis approaches of nanostructures. Here, we studied the effect of grazing angle cross-irradiation Ag thin films for the nanostructures evolution from a top-down approach. Ag thin films of different thicknesses were deposited on Si (100) and glass substrates by electron beam evaporation system and subsequently irradiated at grazing angle ions by 80 keV Ar+in two steps (to induce effectively a cross-ion irradiation). Pristine films exhibited dense and uniform distribution of Ag nanoparticles with their characteristic surface plasmon resonance-induced absorption peak around 420 nm. When the film surfaces were treated with cross-grazing angle irradiation of Ar ions with varying effective fluences from 0.5 × 1017ions/cm2to 2.0 × 1017ions/cm2, it was found that fluence values governed the competition of sputtering and sputter re-deposition of Ag. As a result, lower irradiation fluence favoured the formation of cone-like nanostructures, whereas high fluence values demonstrated dominant sputtering. Fluence-dependent modification of surface features was studied through the Fourier transform infrared spectroscopy and the Rutherford backscattering spectroscopy. Theoretical justifications for the underlying mechanisms are presented to justify the experimental results.

Cite

CITATION STYLE

APA

Kumar, M., Jangid, T., Panchal, V., Kumar, P., & Pathak, A. (2016). Effect of Grazing Angle Cross-Ion Irradiation on Ag Thin Films. Nanoscale Research Letters, 11(1). https://doi.org/10.1186/s11671-016-1665-5

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free