Microstructure of bonding interface for resistance welding of zr-based metallic glass sheets

Abstract

Resistance welding of Zr55Cu30Al10Ni 5 metallic glass sheets was investigated at 723 K in a supercooled liquid region. The welding time was changed from 5 s to 20 s at 723 K. The joint interface of the metallic glass was no defect and no crack. X-ray diffraction technique of the bonding interface of specimens was performed. The specimens showed halo patterns showing existence of only glassy phase, when the welding time was 5 s and 10 s. X-ray diffraction patterns of specimen bonded for 20 s showed crystalline peaks with halo patterns for the welding for 20 s. The crystalline phase at the bonding interface was small. Transmission electron micrograph at the bonding interface showed nanostructures of NiZr2 and Al5Ni3Zr2. © 2009 The Japan Institute of Metals.