Optimization of sodium hydroxide for securing high thermoelectric performance in polycrystalline Sn1 − xSe via anisotropy and vacancy synergy

48Citations
Citations of this article
22Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

The morphology and composition are two key factors to determine the thermoelectric performance of aqueously synthesized tin selenide (SnSe) crystals; however, their controlling is still under exploring. In this study, we report a high figure-of-merit (ZT) of ∼1.5 at 823 K in p-type polycrystalline Sn1 − xSe resulted from a synergy of morphology control and vacancy optimization, realized by carefully tuning the sodium hydroxide (NaOH) concentration during solvothermal synthesis. After a comprehensive investigation on various NaOH concentrations, it was found that an optimized NaOH amount of 10 mL with a concentration of 10 mol L−1 can simultaneously achieve a large average crystal size and a high Sn vacancy concentration of ∼2.5%. The large microplate-like crystals lead to a considerable anisotropy in the sintered pellets, and the high Sn vacancy level contributes to an optimum hole concentration to the level of ∼2.3 × 1019 cm−3, and in turn a high power factor of ∼7.4 μW cm−1 K−2 at 823 K, measured along the direction perpendicular to the sintering pressure. In addition, a low thermal conductivity of ∼0.41 W m−1 K−1 is achieved by effective phonon scattering at localized crystal imperfections including lattice distortions, grain boundaries, and vacancy domains, as observed by detailed structural characterizations. Furthermore, a competitive compressive strength of ∼52.1 MPa can be achieved along the direction of high thermoelectric performance, indicating a mechanically robust feature. This study provides a new avenue in achieving high thermoelectric performance in SnSe-based thermoelectric materials. (Figure presented.).

Cite

CITATION STYLE

APA

Shi, X. L., Liu, W. D., Wu, A. Y., Nguyen, V. T., Gao, H., Sun, Q., … Chen, Z. G. (2020). Optimization of sodium hydroxide for securing high thermoelectric performance in polycrystalline Sn1 − xSe via anisotropy and vacancy synergy. InfoMat, 2(6), 1201–1215. https://doi.org/10.1002/inf2.12057

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free