High-Quality ZnCdS Nanosheets Prepared Using Solvothermal Synthesis

Abstract

For the first time, Zn x Cd 1 - x S nanosheets with different Zn and Cd ion concentrations were prepared using solvothermal synthesis at 200°C for 4 and 24 h. The crystalline structure of the nanosheets was wurtzite. The optical band gaps of the nanosheets increased with increasing Zn ratio; this increase is consistent with the band gaps estimated using Vegard’s formula. The photoluminescence spectra for the 24 h nanosheets had higher emission intensities than those for the 4 h nanosheets. The emission band corresponding to intrinsic near-band-edge emission and a broad peak associated with extrinsic deep-level emission were observed in the photoluminescence spectra.