Load-bearing capacity of zirconia crowns screwed to multi-unit abutments with and without a titanium base: An in vitro pilot study

Abstract

The static and dynamic load-bearing capacities and failure modes of zirconia crowns screwed to multi-unit abutments (MUAs) with and without a titanium base (T-base) were determined. Thirty-six monolithic zirconia crowns screwed to straight MUAs torqued to laboratory analogs (30 Ncm) were assigned to two groups (n = 18). In group A, the zirconia crowns were screwed directly to the MUAs; in group B, the zirconia crowns were cemented to the T-base and screwed to the MUAs. All specimens were aged in 100% humidity (37 ffiC) for one month and subjected to thermocycling (20,000 cycles). Afterwards, the specimens underwent static and dynamic loading tests following ISO 14801. The failure modes were evaluated by stereomicroscopy (20×). There was an unequivocally similar trend in the S-N plots of both specimen groups. The load at which the specimens survived 5,000,000 cycles was 250 N for both groups. Group A failed mainly within the metal, and zirconia failure occurred only at a high loading force. Group B exhibited failure within the metal mostly in conjunction with adhesive failure between the zirconia and T-base. Zirconia restoration screwed directly to an MUA is a viable option, but further studies with larger sample sizes are warranted.