Effect of Different Filler Contents and Printing Directions on the Mechanical Properties for Photopolymer Resins

Abstract

Photopolymer resins are widely used in the production of dental prostheses, but their mechanical properties require improvement. We evaluated the effects of different zirconia filler contents and printing directions on the mechanical properties of photopolymer resin. Three-dimensional (3D) printing was used to fabricate specimens using composite photopolymers with 0 (control), 3, 5, and 10 wt.% zirconia filler. Two printing directions for fabricating rectangular specimens (25 mm× 2 mm× 2 mm) and disk-shaped specimens (φ10 mm× 2 mm) were used, 0° and 90°. Three-point bending tests were performed to determine the flexural strengths and moduli of the specimens. The Vickers hardness test was performed to determine the hardness of the specimens. Tukey’s multiple comparison tests were performed on the average values of the flexural strengths, elastic moduli, and Vickers hardness after one-way ANOVA (α = 0.05). The flexural strengths and elastic moduli at 0° from high to low were in the order of 0, 3, 10, and 5 wt.%, and those at 90° were in the order of 3, 0, 10, and 5 wt.% (p < 0.05). For 5 and 10 wt.%, no significant differences were observed in mechanical properties at 0° and 90° (p < 0.05). The Vickers hardness values at 0° and 90° from low to high were in the order of 0, 3, 5, and 10 wt.% (p < 0.05). Within the limits of this study, the optimal zirconia filler content in the photopolymer resin for 3D printing was 0 wt.% at 0° and 3 wt.% at 90°.