Fabricated CAD/CAM post-core using glass fiber-reinforced resin shows innovative potential in restoring pulpless teeth

Abstract

The prevention of root fractures of pulpless teeth is an important clinical issue to maintain healthy teeth through lifetime. The aim of this study was to examine a clinically effective treatment method for strengthening vulnerable pulpless teeth using CAD/CAM (computer-aided design/com-puter-aided manufacturing) fiber-reinforced post-core by conducting a fracture resistance test. A post-core made with a fiber-reinforced resin disk TRINIA (TR, SHOFU, Kyoto, Japan) was fabricated using a CAD/CAM system. The fiber-layer orientation of the CAD/CAM post-core was paral-lel to the axis of the restored tooth. A post-core using a conventional composite and a fiber post (CF) was also prepared. A fracture resistance test of teeth restored with the post-cores and zirconia crowns was conducted using a universal testing machine, and fracture patterns were identified by micro-CT observation. The fracture load of the roots restored with TR was 1555.9 ± 231.8 N, whereas that of CF was 1082.1 ± 226.7 N. The fracture load of TR was 43.8% that was significantly higher than that of CF (Student’s t-test, p < 0.05). The restored teeth with CAD/CAM resin post-core were found to be repairable even after fracture. These results suggest that the CAD/CAM indirect fiber post-core has the potential to strengthen the vulnerable pulpless teeth.