Application of electrostatic extrusion - flavour encapsulation and controlled release

Abstract

The subject of this study was the development of flavour alginate formulations aimed for thermally processed foods. Ethyl vanilline was used as the model flavour compound. Electrostatic extrusion was applied for the encapsulation of ethyl vanilline in alginate gel microbeads. The obtained microbeads with approx. 10 % w/w of ethyl vanilline encapsulated in about 2 % w/w alginate were uniformly sized spheres of about 450 μm. Chemical characterization by H-NMR spectroscopy revealed that the alginate used in this study had a high content (67 %) of guluronic residues and was rich in GG diad blocks (FGG = 55%) and thus presented a high-quality immobilisation matrix. The thermal behaviour of alginate beads encapsulating ethyl vanilline was investigated by thermogravimetric (TG) and differential scanning calorimetry measurements (TG-DSC) under heating conditions which mimicked usual food processing to provide information about thermal decomposition of alginate matrix and kinetics of aroma release. Two well resolved weight losses were observed. The first one was in the 50-150°C temperature range with the maximum at approx. 112°C, corresponding to the dehydration of the polymer network. The second loss in the 220-325°C temperature range, with a maximum at ∼ 247°C corresponded to the release of vanilline. The obtained results indicate that up to 230°C most of the vanilline remained intacta, while prolonged heating at elevated temperatures led to the entire loss of the aroma compound. © 2008 by MDPI.