Characterization of lignin-derived products from Japanese beech wood as treated by two-step semi-flow hot-compressed water

Abstract

Japanese beech (Fagus crenata) wood was treated by two-step semi-flow hot-compressed water (the first stage: 230 °C/10 MPa/15 min, the second stage: 270 °C/10 MPa/15 min), and produced lignin-derived products in the hot-compressed water-soluble portions at the first and second stages, and the final residue of the second stage was characterized with alkaline nitrobenzene oxidation method and gel permeation chromatographic analysis. As a result, the lignin-derived products at the first stage, where hemicellulose was also decomposed, consisted of lignin-based monomers and dimers and oligomers/polymers in the water-soluble portion. A large part of the oligomers/polymers was, however, recovered as the precipitate during 12 h setting after hot-compressed water treatment. By the analysis of nitrobenzene oxidation products, there were relatively higher contents of ether-type lignin in the precipitate at the first stage than in original beech wood. Since the ether linkages of lignin are more preferentially cleaved by this hot-compressed water, lignin-based polymeric fractions were flowed out from the porous cell walls from which hemicellulose was removed. On the other hand, at the second stage condensed-type lignin remained in the precipitate and residue. Based on these results, decomposition behavior of lignin in Japanese beech wood as treated by the two-step semi-flow hot-compressed water was discussed regarding the topochemistry of lignin structure. © 2012 The Japan Wood Research Society.