Hardness of densified wood in relation to changed chemical composition

Abstract

The aim of this study was to evaluate some of the properties of densified poplar and birch wood earlier subjected to partial delignification of cell walls. The effects of delignification are presented as a comparison of the content of basic structural components in wood before and after chemical modification. In birch wood, the lignin content decreased by 20%, while that of cellulose decreased by 9.7% and that of hemicellulose decreased by 64.9%. In poplar, the lignin content decreased by 34.1%, that of cellulose decreaed by 13.5%, and that of hemicellulose decreased by 58.0%. The hardness of densified birch and poplar wood, after partial reduction of chemical components, was 147 and 111 MPa, respectively, and, compared with natural (non-densified) wood, was almost 4.5 times and 7 times higher, respectively. Poplar wood was more densified (without delignification 238% and after delignification 281%). In the case of birch wood, the density levels were 176% and 188%, respectively.