In the preparation and evaluation of Fischer- Tropsch (FT) catalysts, active catalysts formed by both incipient wetness impregnation (IWI) and atomic layer deposition (ALD) of major components were demonstrated. ALD-deposited Co on a silica support was more effective than a similar catalyst deposited upon a support of ALD-deposited Al 2O 3 on silica. The addition of Co reduction promoters including Pt, Ir and Ru using either ALD or IWI has been shown to strongly affect the catalyst pre-conditioning step. CO conversion results were consistent with previously reported Temperature Programmed Reduction X-ray Absorption Near-edge Structure/Extended X-ray Absorption Fine Structure Spectroscopy (TPRXANES/ EXAFS) experiments observing the nature of chemical transformations occurring during the activation of cobalt-based FT catalysts in hydrogen. Specifically, there exists a 2-step reduction process involving Co 3O 4 to Co O and Co O to Co 0 transformations. The extent of catalyst preconditioning was strongly affected by the reduction temperature (with 400 °C preferred) and the loading of the promoter. This was demonstrated using a continuous-flow catalytic-bed unit with a 2:1 molar blend of H2:CO, at temperatures ranging from about 260 to 300 °C, pressures averaging 1.3 MPa (190 psia), and gas space velocities about 24 NL/h-g. © 2012 Springer Science+Business Media, LLC.
CITATION STYLE
Cronauer, D. C., Elam, J. W., Jeremy Kropf, A., Marshall, C. L., Gao, P., Hopps, S., … Davis, B. H. (2012). Fischer-tropsch synthesis: Preconditioning effects upon co-containing promoted and unpromoted catalysts. Catalysis Letters, 142(6), 698–713. https://doi.org/10.1007/s10562-012-0818-0
Mendeley helps you to discover research relevant for your work.