Impact of structural defects on the surface quality of hardwood species sliced veneers

Abstract

The surface roughness constitutes one of the most critical properties of wood and wood veneers for their extended utilization, affecting the bonding ability of the veneers with one another in the manufacturing of wood composites, the finishing, coating and preservation processes, and the appearance and texture of the material surface. In this research work, logs of five significant European hardwood species (oak, chestnut, ash, poplar, cherry) of Balkan origin were sliced into decorative veneers. Their surface roughness was examined by applying a stylus tracing method, on typical wood structure areas of each wood species, as well as around the areas of wood defects (knots, decay, annual rings irregularities, etc.), to compare them and assess the impact of the defects on the surface quality of veneers. The chestnut veneers presented the smoothest surfaces, while ash veneers, despite the higher density, recorded the highest roughness. In most of the cases, the roughness was found to be significantly lower around the defects, compared to the typical structure surfaces, probably due to lower porosity, higher density and the presence of tensile wood. The results reveal that the presence of defects does not affect the roughness of the veneers and increases neither the processing requirements of the veneer sheets before finishing, nor the respective production cost of veneers and the veneer-based wood panels. The high utilization prospects of the examined wood species in veneer production, even those bearing various defects, is highlighted.