The synthesis of nonionic hyperbranched organosilicone surfactant and characterization of itswetting ability

Abstract

In this research, the epoxy silicone oil and self-made hydroxyl-terminated hyperbranched polymer (HBP-OH) were used to synthesis the nonionic hyperbranched organosilicone surfactant (NHSi). The molar rate of hydroxyl groups of HBP-OH and epoxy groups of epoxy silicon oil (n-OH: n-epoxy) was adjusted from 5:1~60:1 to prepare a series of NHSi. The Gel Permeation Chromatography (GPC), Fourier Transform Infrared Spectroscopy (FT-IR), contact angle measuring instrument, surface tensiometer and Scanning Electron Microscope (SEM) were employed to characterize the structure and property of HBP-OH and NHSi. GPC analysis indicated that the Mn of HBP-OH was 340.5. FT-IR analysis showed that with the increase of molar rate of n-OH:n-epoxy, the peak intensity of -OH increased. The prepared NHSi was then used to prepare the water solution. The lowest surface tension of NHSi solution was 24.71 mN.m-1 when the n-OH:n-epoxy was 30:1 in the preparation process. The minimum water contact angle of waterborne polyurethane (WPU) emulsion by adding 2% of NHSi was 14.85° on the surface of glass. The wetting experiments showed that the NHSi has good wetting ability to fixed sea-island superfine fiber synthetic material.