Size-dependent structure and magnetic properties of DyMnO3 nanoparticles

Abstract

The structure and magnetic properties of orthorhombic DyMnO3 nanoparticles with different particle sizes are investigated in this paper. With decreasing particle size, all the lattice parameters a, b, and c gradually decrease, whereas the orthorhombic distortion increases. Magnetic measurements reveal that the antiferromagnetic interaction of Mn ions is weakened due to the decrease in Mn-O-Mn bond angle. Above a critical field H, DyMnO3 undergoes a field-induced metamagnetic transition at 4 K, which is related to the spin reversal of Dy moments. The critical field H∗ increases monotonically with size reduction, indicating an enhancement of the antiferromagnetic interaction of Dy ions due to the decreased distance between rare earth ions. The magnetization at 4 K and 5 T, i.e., M(4 K, 5 T) shows a non-monotonic variation with particle size d, i.e., M(4 K, 5 T) initially increases with size reduction but decreases again for d < 68 nm. A modified core-shell model, in which the ferromagnetic ordering (Dy magnetic structure) and antiferromagnetic ordering (Mn magnetic structure) coexist in the core, is proposed to explain this behavior.