Morphotropic phase boundary in epitaxial Pb (Zr,Ti) O3 thin films: Two-dimensional planar size effect

Abstract

The epitaxial Pb (Zr,Ti) O3 (PZT) thin films were patterned into small islands by a photolithographic process, and the morphotropic phase boundary (MPB) in which the tetragonal and rhombohedral phases coexist was realized by changing the two-dimensional planar sizes. The MPB moved toward the Zr-rich composition due to two-dimensional film stress in the continuous epitaxial PZT thin films. The 600-nm -thick epitaxial Pb (Zr0.55 Ti0.45) O3 and Pb (Zr0.60 Ti0.40) O3 films were found highly rich in tetragonal phase. As the films were patterned progressively in smaller sizes and the misfit strains were relaxed further accordingly, the MPB was restored to the original bulk composition, showing higher fractions of rhombohedral phase. In the epitaxial Pb (Zr0.55 Ti0.45) O3 film, two-dimensional patterns of 100×100, 10×10, and 5×5 μ m2 were found within the MPB region, whereas the smallest 2×2 μ m2 patterns were fully rhombohedral. On the other hand, in the epitaxial Pb (Zr0.60 Ti0.40) O3 film, only the 100×100 μ m2 patterns belonged to MPB rich in tetragonal phase, while the smaller patterns exhibited fully rhombohedral phases. © 2005 American Institute of Physics.