Effect of Curing Temperature on High-Strength Metakaolin-Based Geopolymer Composite (HMGC) with Quartz Powder and Steel Fibers

Abstract

Geopolymer is a new type of synthesized aluminosilicate material. Compared with ordinary Portland cement, it has better fire resistance and durability, and is more environmentally friendly. In this paper, a high-strength metakaolin-based geopolymer composite (HMGC) has been developed by utilizing quartz powder and steel fibers. The optimization compositions and effect of curing temperatures (from ambient temperature to 90◦ C) on the strength performance of the HMGC is studied. The optimized 1-day compressive strength of the HMGC can reach 80 MPa, and the 3-day compressive strength is close to 100 MPa (97.49 MPa). Combined with XRD, FTIR, SEM and MIP characterization, the mechanisms behind the strength development under different curing temperatures are analyzed. The results show that heat curing can significantly speed up the process of geopolymerization and increase the early strength of the HMGC. However, long-term heat curing under high temperature (such as 90◦ C, 7 days) would reduce the mechanical strength of the HMGC. Prolonged high-temperature curing increases the pores and micro-defects in the gel phase of the HMGC, which may be attributed to chemical shrinkage. Thus, the curing temperature should be carefully controlled to make a HMGC with better performance.