The aim of this study was to use the isobornyl methacrylate (IBOMA) as a combining or substituent diluent monomer in the resin matrix of dental resin composites. Thus, the resin matrix was formulated with 60 wt% of BisGMA and 40 wt% of diluent monomers. TEGDMA as the only diluent monomer was used as control with 40 wt%, while total substitution of TEGDMA was done with 40 wt% of IBOMA. The combination of IBOMA and TEGDMA was done with 20 wt% of each monomer. To the resin matrix, 65 wt% of filler particles was added. Degree of conversion (DC) using FT-IR, flexural strength (FS), flexural modulus (FM), polymerization shrinkage by gap formation (GF), Knoop hardness (KH) and solvent degradation (SD) were evaluated. Data were analyzed using ANOVA and Tukey’s test (α=0.05; b=0.2). The results showed that reducing or substituting TEGDMA using IBOMA did not affect the DC (0.085), FS (p=0.886) or FM (p=0.414). Also, when IBOMA was used, lower GF was found in comparison to the control containing only TEGDMA as the diluent monomer (p=0.032). However, even though all composites presented reduction in KH during the SD test, the combination of IBOMA and TEGDMA showed similar reduction in KHN in comparison to the control group (p=0.001), while the total substitution of TEGDMA with IBOMA decreased KHN after SD (p=0.041). Thus, the combination of IBOMA and TEGDMA seem to reduce SD and GF without affecting the properties of resin composites.
CITATION STYLE
Favarão, J., de Oliveira, D. C. R. S., Rocha, M. G., Zanini, M. M., Abuna, G. F., Mendonça, M. J., & Sinhoreti, M. A. C. (2019). Solvent degradation and polymerization shrinkage reduction of resin composites using isobornyl methacrylate. Brazilian Dental Journal, 30(3), 272–278. https://doi.org/10.1590/0103-6440201802525
Mendeley helps you to discover research relevant for your work.