Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. Objective: The purpose of this study was to evaluate the microtensile bond strength (μTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (eDTA). Material and Methods: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% eDTA. The specimens received the self-etching adhesive system (XeNO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. Results: Mean μTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/ F=22.5763). The application of 1% NaOCl/17% eDTA resulted in statistically similar μTBS to the control group. Conclusions: None of the irrigants affected negatively the μTBS of XeNO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% eDTA produced similar bond strength to that of untreated dentin.
CITATION STYLE
Cecchin, D., Farina, A. P., Galafassi, D., Barbizam, J. V. B., Corona, S. A. M., & Carlini-Júnior, B. (2010). Influence of sodium hypochlorite and EDTA on the microtensile bond strength of a self-etching adhesive system. Journal of Applied Oral Science, 18(4), 385–389. https://doi.org/10.1590/S1678-77572010000400011
Mendeley helps you to discover research relevant for your work.