Assessment of ageing effect on the mechanical behaviour of steel/aluminium self-piercing riveted joint

7Citations
Citations of this article
17Readers
Mendeley users who have this article in their library.

This article is free to access.

Abstract

Background: Self-piercing riveting (SPR) is a new performing technology able to joint several kinds of metal and non-metal supports together. The combined effect of joint configuration and environmental conditions could have detrimental effect on the ageing effect on mechanical behaviour of dissimilar metal SPR joints. Methods: The joining of dissimilar materials, such as steel and aluminium, realized by self-piercing riveting (SPR) technique was studied to evaluate the ageing effects on its mechanical behaviour in critical environmental conditions. The investigation was carried out on symmetrical or unsymmetrical joints at varying total thicknesses (i.e. 2.0, 2.5 and 3.0 mm). The joint resistance was determined by single-lap shear tests. A design of experiment (DoE) has been performed by using MinitabĀ® followed by the statistical analysis (ANOVA) of the experimental data. Long-term ageing tests in salt spray environment were performed to evaluate the durability of the mechanical joint. Results: The experimental results evidenced that the corrosion degradation phenomena influenced significantly both the performance and failure mechanisms of the joints; also, the joint configuration is a significant factor for the corrosion effect. In the salt spray, the aluminium sheet undergoes a noticeable degradation due to galvanic Al/Fe corrosion. The set characterized by thinner aluminium sheet evidenced a gradual reduction of the mechanical strength with increasing ageing time due to the prevalence of thinning induced by aluminium corrosion. Instead, for S10-A15 samples (characterized by a thicker thickness of aluminium sheet) during the first 7 weeks, stable mechanical performances were observed. Conclusions: The experimental results evidenced that the corrosion degradation phenomena influence significantly both performances and failure mechanisms of SPR joints. Furthermore, the durability of the SPR joint is strongly affected by the joint configuration, and the best results were observed in the unsymmetrical joint with thicker aluminium sheet.

Cite

CITATION STYLE

APA

Calabrese, L., Proverbio, E., Di Bella, G., Galtieri, G., & Borsellino, C. (2015). Assessment of ageing effect on the mechanical behaviour of steel/aluminium self-piercing riveted joint. International Journal of Mechanical and Materials Engineering, 10(1). https://doi.org/10.1186/s40712-015-0034-y

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free