Pengaruh Variasi Temperatur Quenching pada Aluminium Paduan AlMgSi-Fe12% terhadap Keausan

  • Wardoyo W
  • Sumpena S
N/ACitations
Citations of this article
64Readers
Mendeley users who have this article in their library.

Abstract

The purpose of this research is to determine the effect of heat treatment hardening of Al Mg Si - Fe12% casting aluminium alloys on wear. The tests were carried out on specimens of raw materials and heat-treated specimens with variations of temperature used were 550 o C, 575 o C, 600 o C, and 625 o C, and used 15 minutes of holding time in each heat treatment, then quenching in SAE 20 oil. The method used for wear-tested was high speed ogoshi universal testing machine wear. The result had shown on raw material a specific wear rate was 2.256102E-07 mm 2 /kg. Test results on the specimens that have received heat treatment hardening temperature 550 o C increased the wear value decreased to 1.7471E-07 mm 2 /kg. In materials with temperature heat treatment, 575 o C causes wear values were increased when compared with raw material, respectively, 2,83739E-07 mm 2 /kg. In materials with temperature heat treatment 600 o C also causes wear values were increased when compared with raw material, respectively, 2,65105E-07 mm 2 /kg. Test results on the test material that ha s received heat treatment temperature 625 o C increased the wear value decreased to 2.16777E-07 mm 2 /kg.

Cite

CITATION STYLE

APA

Wardoyo, W., & Sumpena, S. (2018). Pengaruh Variasi Temperatur Quenching pada Aluminium Paduan AlMgSi-Fe12% terhadap Keausan. Jurnal Engine: Energi, Manufaktur, Dan Material, 2(1), 33. https://doi.org/10.30588/jeemm.v2i1.528

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free