Effect of silver nanoparticles, zinc oxide nanoparticles and titanium dioxide nanoparticles on microshear bond strength to enamel and dentin

Abstract

Aim: This study was aimed to evaluate whether antibacterial pretreatment of enamel and dentin with silver nanoparticles (SNPs), zinc oxide nanoparticles (ZNPs) and titanium dioxide nanoparticles (TNPs) has any effect on the microshear bond strength of an etch-and-rinse adhesive system. Materials and methods: Eighty human third molars were randomly assigned to eight subgroups (n = 10). Enamel groups included no pretreatment (E), pretreatments with SNPs (ESNP), ZNPs (EZNP) and TNPs (ETNP) before acid etching and adhesive application. Dentinal groups included no pretreatment (D), pretreatments with SNPs (DSNP), ZNPs (DZNP) and TNPs (DTNP). The specimens were bonded by Adper Single Bond and polyvinyl chloride microtubes and were restored with Z250 composite. The bonded surfaces underwent microshear bond strength (μSBS) test. Data in megapascal (MPa) were analyzed with the Kruskal-Wallis test and the Mann-Whitney test (p = 0.05). Results: There was not a significant difference among the groups in enamel (p > 0.05). There was no significant difference between the application of three nanoparticles and the control group in dentin. However, DSNPs had a higher μSBS (25.60 ± 14.61) than that of the DZNPs and DTNPs groups (p = 0.03 and p = 0.001, respectively). Also, the mean μSBS value was lower in dentin groups compared to the respective enamel groups (p < 0.05) except for groups DSNPs and ESNPs in which no significant difference was found (p > 0.05). Conclusion: Pretreatment with SNPs, TNPs, and ZNPs can be suggested to achieve potent antibacterial activities without compromising the bond strength. The best result was obtained for pretreatment with SNPs compared to pretreatment with TNPs or ZNPs in dentin and enamel, albeit the differences were not significant in the enamel groups. Clinical significance: Effective antibacterial treatment prior to adhesive bonding application is desirable to provide successful restoration if it would not adversely affect the bond strength of the adhesive system. Nanoparticles can be applied to meet this goal.