Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: A comparative in vitro study

Abstract

Background: Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. Methods: Five test groups (n = 22) were formed by using the indicated CAD/CAM blocks: VITA Enamic (VITA Zahnfabrik), Lava Ultimate (3 M ESPE), IPS e.max CAD (Ivoclar Vivadent), IPS Empress CAD (Ivoclar Vivadent), and VITA Mark II (VITA Zahnfabrik). Two specimens from each test group were used for XRD and EDS analysis. Remaining samples were divided into two subgroups (n = 10). One subgroup specimens were thermocycled (5 °C to 55 °C, 30s, 10,000 cycles) whereas the other were not. All of the specimens were evaluated in terms of flexural strength, Vickers hardness, and fracture toughness. Results were statistically analyzed using two-way ANOVA, one-way ANOVA, Tukey's HSD, and Student's t tests (α =.05). Fractured specimens were evaluated using SEM. Results: The highest Vickers microhardness value was found for VITA Mark II (p