Surface Damage Characteristics of BK7 Glass in Ultrasonic Vibration Machining Based on Scratching Experiment

Abstract

To further explore the material removal mechanism in ultrasonic vibration machining, a diamond Vickers indenter was used to carry out scratching experiment for BK7 glass specimen. The morphologies of scratches and removal mechanism of material were analysed under different conditions. The results showed that the damage mode of scratch was plastic deformation when the scratching depth was small enough, and no crack was observed. With increase of scratching depth, the intermittent and continuous scratches appeared in plastic removal area, and plastic flow phenomenon was obvious. With further increase of scratching depth, the median/radial cracks and lateral cracks were induced, and the material was removed by plastic flow and brittle-plastic mixed mode. When the indenter arrived at the brittle fracture removal area, cracks in scratched surface became denser, the lateral cracks extended from inside of material to workpiece surface, and the material was removed by brittle fracture.