Can the silane heat treatment influence the bond durability between resin cements and a dental ceramic?

Abstract

ABSTRACT Objective Evaluate the influence of silane heat treatment in bond durability between two resin cements and CAD/CAM feldspathic ceramic. Methods 40 feldspathic ceramic blocks were obtained, and were duplicated in microhybrid composite. All ceramic blocks were etched with 10% hydrofluoric acid for 20 s and received application of silane agent. The blocks were randomizedinto eight groups (n=5) according to the surface treatments and luting agents: P- Panavia F; PAg- Panavia F + Aging; HP- Heat Treatment + Panavia F; HPAg- Heat Treatment + Panavia F + Aging; R- RelyX ARC; Rag- RelyX ARC + Aging; HR- Heat Treatment + RelyX ARC; HRAg- Heat Treatment + RelyX ARC + Aging. The heat treatment was performed in furnace at 100 °C for 2 min. All blocks were cemented and cut to obtain samples with adhesive area of 1 mm2. Aging was performed with 10000 thermal cycles. The samples were subjected to microtensile bond strength test. Results The three-way ANOVA test revealed a significant interaction between cement versus heat treatment (p=0.001) and heat treatment versus thermal cycling (p=0.001) indicating that there was a change in bond strength due to surface treatment and aging. Conclusion Therefore, the heat treatment of the silane at 100 ºC for 2 minutes obtained higher values of bond strength between the resin cement and a feldspathic ceramicafter aging.RESUMO Objetivo Avaliar a influência do tratamento térmico do silano na resistência de união entre dois cimentos resinosos e uma cerâmica feldspática CAD/CAM. Métodos Quarenta blocos cerâmicos foram duplicados em resina micro-híbrida. Todas as cerâmicas foram condicionadas com ácido fluorídrico 10% por 20 s e receberam aplicação do silano. Os blocos foram randomizados em oito grupos (n = 5): P-Panavia F; PAg- Panavia F + Envelhecimento; HP-Tratamento térmico + Panavia F;HPAg-Tratamento térmico + Panavia F + Envelhecimento; R-RelyX ARC; RAg-RelyX ARC; HR-Tratamento térmico + RelyX ARC; HRAg - Tratamento térmico + RelyX ARC + Envelhecimento. O tratamento térmico foi realizado em forno a 100 °C durante2 min. Todos os blocos foram cimentados e cortados para obter amostras para microtração. Foram feitos 10000 ciclos térmicos. As amostras foram submetidas a teste de micro-tração. Resultados O teste ANOVA revelou uma interação significativa entre cimento/tratamento térmico (p=0,001) e tratamento térmico/ciclo térmico (p=0,001). Conclusão Dessa maneira, o tratamentotérmico do silano a 100ºC por 2 minutos foi capaz de aumentar a resistência de união entre o cimento resinoso e uma cerâmica feldspática mesmo após o envelhecimento.