We report a comparative spectroscopic study on the thin films of epitaxial aluminum nitride (AlN) on basal plane sapphire (Al2O3) substrates grown in hydrogen (H2) and nitrogen (N2) gas reaction environments. AlN films of similar thicknesses (~3.0 µm) were grown by metal-organic chemical vapor deposition (MOCVD) for comparison. The impact of the gas environment on the AlN epilayers was characterized using high-resolution X-ray diffraction (HR-XRD), X-ray photoelectron spectroscopy (XPS), Raman scattering (RS), secondary ion mass spectroscopy (SIMS), cathodoluminescence (CL), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The study showed that AlN layers grown in a N2 environment have 50% less stress (~0.5 GPa) and similar total dislocation densities (~109/cm2) as compared to the films grown in a H2 environment. On the other hand, AlN films grown in a H2 gas environment have about 33% lesser carbon and 41% lesser oxygen impurities than films grown in a N2 growth environment. The possible mechanisms that influenced the structural quality and impurity incorporation for two different gas environments to grow AlN epilayers in the MOCVD system on sapphire substrates were discussed.
CITATION STYLE
Hasan, S., Jewel, M. U., Karakalos, S. G., Gaevski, M., & Ahmad, I. (2022). Comparative Spectroscopic Study of Aluminum Nitride Grown by MOCVD in H2 and N2 Reaction Environment. Coatings, 12(7). https://doi.org/10.3390/coatings12070924
Mendeley helps you to discover research relevant for your work.