Extraction of gelatin from catfish bone using NaOH and its utilization as a template on mesoporous silica alumina

Abstract

Gelatin extraction from catfish bone using NaOH and its utilization as a template on a synthesis of mesoporous silica-alumina had been investigated. The extraction was prepared by immersing 25 g catfish bone in 125 mL of NaOH in concentration of 0.0; 0.05; 0.10; 0.15 and 0.20 M for 24 h, then washing with demineralized water until pH 7, followed by immersed the bone into 125 mL of 1 M HCl for 1 h, then washed using demineralized water into pH 5. To produce gelatin the bone was refluxed with 100 mL demineralized water at 70°C for 5 h then evaporated at 50°C. The dry gelatin was characterized using FTIR and electrophoresis (SDS-PAGE). The best performance of gelatin was produced by NaOH 0.10 M. The gelatin consists of amide A, B, I, II, III and molecular weight of 25-200kDa. Silica and Alumina material prepared from Lapindo mud extraction. Dry Lapindo mud crushed and filtered until pass 100 mesh, then reflux using 6 M HCl (1:4 w/V) at 90°C for 5h then filtered. The filtrate was consisting alumina solution adding with 6 M NaOH (2/3 V/V) them filtered. The filtrate then injected by CO2 gas for 30 minutes and filtered, the residue was calcined at 500°C for 5h. The residual of Lapindo mud dried and refluxed with 6 M NaOH (1:4 w/v) at 90 °C. After 5h filtered and the filtrate added by HCl to pH 8 and filtered, the residual then dried. The Si and Al were then analyzed by XRF and consist of silica and alumina for 99.1 and 87.73%, respectively. Silica-alumina was prepared using silica and alumina extracted from Lapindo mud. 6 g of SiO2 and 2 g of NaOH was immersed in 62 mL of demineralized water then added with alumina solution (0.204 g alumina in 30 mL demineralized water). The gelatin solution (5 g gelatin in 70 mL demineralized water) was dropped into the silica-alumina while stirring at 50°C for 4 h and aging for 24 h. The synthesized silica alumina was analysed using FTIR and surface area analyser. The FT-IR spectra indicated the TO4 (T=Si, Al) vibration at wave number of 1049.28 and 1103.23 cm-1. The synthesized silica-alumina showed mesoporous characters with a pore diameter of 41.18 nm and surface area of 32.76 m2/g.