Influence of the Addition of Spruce Fibers to Industrial-Type High-Density Fiberboards Produced with Recycled Fibers

Abstract

Abstract: The growing production of wood-based panels and the linked consumption result in a need for substituting standard wooden raw materials. The shortage of wood availability, as well as the increasing prices and a trend towards more environmentally friendly materials and processes, have encouraged the producers of wood-based products to consider extending the life cycle of wood composites. In the present work, the influence of substituting pine with spruce for industrial high-density fiberboards with 5% of recovered fibers was studied. Samples containing 0%, 25%, 50%, and 100% spruce fibers were tested in their mechanical resistance and their interaction with water. Boards from all samples met relevant standard requirements; however, the addition of spruce caused a decrease in mechanical properties, with homogeneity having the most significant influence. The modulus of rupture dropped up to 6% and the internal bond for 47% for samples having 50% of spruce. The most significant drop (50%) was observed for surface soundness for samples made with 100% spruce. Regarding physical properties, swelling increased up to 19% with 50% spruce; on the other hand, its water absorption decreased for up to 12%. The addition of spruce to industrial high-density fiberboards also influenced the formaldehyde content negatively, with an increase of up to 21% with 50% spruce. Graphic Abstract: [Figure not available: see fulltext.].