Effect of 2024 Al Alloy insert on the grain refinement of a 2024 Al Alloy prepared via insert mold casting

Abstract

In this study, an insert mold casting was fabricated by inserting 2024 Al extruded rods into a 2024 Al melt. The molds were kept at a 2024 Al melt for different times. The 2024 Al extruded rods were used to refine the 2024 Al alloy grains because the advantage of this method is that it is contamination free compared with other grain refiners. Moreover, we investigated the macro and microstructure of the ingots. Further, we analyzed the refinement mechanism of the 2024 Al rod on the 2024 Al alloy. Our result showed that when the immersion time of the 2024 Al insert was 0 s, a metallurgical bonding was partly formed between the 2024 Al insert and the 2024 Al alloy mold cast. When the immersion time of the 2024 Al insert increased to 5 s, the 2024 solid insert was dissolved in the liquid; the coarse dendritic grains were replaced by fine equiaxed grains. The refinement mechanism for the insertion of a 2024 Al rod on the 2024 Al alloy was to melt the 2024 Al insert and have it decrease the degree of the liquid superheat, which thus increased the cooling rate and provided a large number of small particles that acted as the nucleus of heterogeneous nucleation. However, these particles were melted gradually in the high-temperature liquid after an increase of immersion time. Thus, the refinement effect of 2024 Al insert on the solidified structure was weakened.