The crystal structure and chemical bonding of magnetron-sputtering deposited nickel carbide Ni$_{1-x}$C$_{x}$ (0.05$\leq$x$\leq$0.62) thin films have been investigated by high-resolution X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy, and soft X-ray absorption spectroscopy. By using X-ray as well as electron diffraction, we found carbon-containing hcp-Ni (hcp-NiC$_{y}$ phase), instead of the expected rhombohedral-Ni$_{3}$C. At low carbon content (4.9 at\%) the thin film consists of hcp-NiC$_{y}$ nanocrystallites mixed with a smaller amount of fcc-NiC$_{x}$. The average grain size is about 10-20 nm. With the increase of carbon content to 16.3 at\%, the film contains single-phase hcp-NiC$_{y}$ nanocrystallites with expanded lattice parameters. With further increase of carbon content to 38 at\%, and 62 at\%, the films transform to X-ray amorphous materials with hcp-NiC$_{y}$ and fcc-NiC$_{x }$ nanodomain structures in an amorphous carbon-rich matrix. Raman spectra of carbon indicate dominant $sp^{2}$ hybridization, consistent with photoelectron spectra that show a decreasing amount of C-Ni phase with increasing carbon content. The Ni $3d$ - C $2p$ hybridization in the hexagonal structure gives rise to the salient double-peak structure in Ni $2p$ soft X-ray absorption spectra at 16.3 at\% that changes with carbon content. We also show that the resistivity is not only governed by the amount of carbon, but increases by more than a factor of two when the samples transform from crystalline to amorphous.

Cite

CITATION STYLE

APA

Furlan, A., Lu, J., Hultman, L., Jansson, U., & Magnuson, M. (2014). Crystallization characteristics and chemical bonding properties of nickel carbide thin film nanocomposites. Journal of Physics Condensed Matter, 26(41). https://doi.org/10.1088/0953-8984/26/41/415501

Register to see more suggestions

Mendeley helps you to discover research relevant for your work.

Already have an account?

Save time finding and organizing research with Mendeley

Sign up for free