Electrochemical and sulfide stress corrosion cracking behaviors of tubing steels in a H2S/CO2 annular environment

Abstract

The electrochemical and sulfide stress corrosion cracking (SSCC) behaviors of 13Cr stainless steel and P110 steel were investigated in a simulated acidic annular environment with low-temperature and high-pressure H2S/ CO2 using electrochemical methods, U-bend immersion tests, and scanning electron microscopy. In the solution containing high pressure CO 2, 13Cr, and P110 steels exhibited general corrosion and severe pitting, respectively. Compared with sweet corrosion, additional H2S in the solution enhanced the corrosion of 13Cr steel but inhibited the corrosion of P110 steel. By contrast, in a solution containing 4 MPa CO2 and different PH2S (0-0.3 MPa), the susceptibility of both 13Cr stainless steel and P110 steel toward SSCC was significantly promoted by increases in H2S partial pressure. The 13Cr stainless steel exhibited higher susceptibility toward SSCC than P110 steel under a H2S/CO2 environment but lower susceptibility under a pure CO2 environment. © 2014 The Author(s).