Additive Manufacturing of Cu Using Graphene-Oxide-Treated Powder

Abstract

Additive manufacturing of Cu is interesting for many applications where high thermal and electric conductivity are required. A problem with printing of Cu with a laser-based process is the high reflectance of the powder for near-infrared wavelengths making it difficult to print components with a high density. In this study, we have investigated laser bed fusion (L-PBF) of Cu using graphene oxide (GO)-coated powder. The powder particles were coated in a simple wet-chemical process using electrostatic attractions between the GO and the powder surface. The coated powder exhibited a reduced reflectivity, which improved the printability and increased the densities from ~90% for uncoated powder to 99.8% using 0.1 wt% GO and a laser power of 500 W. The coated Cu powders showed a tendency for balling using laser powers below 400 W, and increasing the GO concentration from 0.1 to 0.3 wt.% showed an increase in spattering and reduced density. Graphene-like sheet structures could be observed in the printed parts using scanning electron microscopy (SEM). Carbon-filled inclusions with sizes ranging from 10–200 nm could also be observed in the printed parts using transmission electron microscopy (TEM). The GO treatment yielded parts with higher hardness (75.7 HV) and electrical conductivity (77.8% IACS) compared to the parts printed with reference Cu powder.